Phenolic Reinforced Molding Compound 4330-3 Shunds
Tlhaloso ea Sehlahisoa
4330-3, sehlahisoa se sebelisoa haholo bakeng sa ho bopa, ho hlahisa matla, literene, lifofane, le liindasteri tse ling tse sebelisoang habeli, joalo ka likarolo tsa mochini, tse nang le matla a phahameng a mochini, mocheso o phahameng, mocheso o phahameng, ho hanyetsa mocheso o tlase le litšobotsi tse ling.
Sehlahisoa sena ke motsoako oa ho bopa oa thermosetting o entsoeng ka resin ea phenolic kapa resin ea eona e fetotsoeng e le binder, e nang le khoele ea khalase e se nang alkali le lisebelisoa tse ling.
Litlhaloso tsa Sehlahisoa
| Tekanyetso ea Teko | JB/T5822- 2015 | |||
| NO. | Lintho tsa Tlhahlobo | Yuniti | BH4330-1 | BH4330-2 |
| 1 | Litaba tsa Resin | % | E ka buisanoa | E ka buisanoa |
| 2 | Litaba tse Fetang | % | 4.0-8.5 | 3.0-7.0 |
| 3 | Botenya | g/cm3 | 1.65-1,85 | 1.70-1,90 |
| 4 | Ho Monyeha ha Metsi | % | ≦0.2 | ≦0.2 |
| 5 | Martin Mocheso | ℃ | ≧280 | ≧280 |
| 6 | Matla a Kobehang | MPa | ≧160 | ≧450 |
| 7 | Matla a Tšusumetso | KJ/m2 | ≧50 | ≧180 |
| 8 | Matla a tšepe | MPa | ≧80 | ≧300 |
| 9 | Bokaholimo ba Resistivity | Ω | ≧10×1011 | ≧10×1011 |
| 10 | Ho hanyetsa Molumo | Ω.m | ≧10×1011 | ≧10×1011 |
| 11 | Seaparo se mahareng (1MHZ) | - | ≦0.04 | ≦0.04 |
| 12 | Tumello e Lekaneng (1MHZ) | - | ≦7 | ≦7 |
| 13 | Matla a Dielectric | MV/m | ≧16.0 | ≧16.0 |
Storge
E lokela ho bolokoa ka phaposing e ommeng le e nang le moea o kenang moo mocheso o sa feteng 30 ℃.
U se ke ua haufi le mollo, ho futhumatsa le khanya ea letsatsi e tobileng, e eme e bolokiloe sethaleng se khethehileng, stacking e otlolohileng le khatello e boima e thibetsoe ka ho feletseng.
Bophelo ba sethala ke likhoeli tse peli ho tloha ka letsatsi la tlhahiso. Kamora nako ea polokelo, sehlahisoa se ntse se ka sebelisoa kamora ho feta tlhahlobo ho latela maemo a sehlahisoa. Tekanyetso ea tekheniki: JB/T5822-2015