Lithapo tse tala tse thehiloeng ho PAN li hloka ho ba le oxidized pele, mocheso o tlase oa carbonized, le mocheso o phahameng oa carbonized ho theha.likhoele tsa carbon, ebe e etsoa graphite ho etsa likhoele tsa graphite. Thempereichara e fihla ho 200 ℃ ho ea ho 2000-3000 ℃, e etsang maikutlo a fapaneng le ho etsa libopeho tse fapaneng, tseo le tsona li nang le thepa e fapaneng.
1. Mokhahlelo oa pyrolysis:Pre-oxidation karolong ea mocheso o tlase, mocheso o tlase oa carbonization karolong ea mocheso o phahameng
Pre-oxidation arylation e etsahala, bolelele ba metsotso e ka bang 100, mocheso oa 200-300 ℃, sepheo ke ho thermoplastic PAN linear macromolecular ketane ka har'a sebopeho sa trapezoidal se sa keneleng mocheso oa polasetiki, karabelo ea mantlha bakeng sa ketane ea macromolecular ea cyclization le molek'hule e mengata e tsamaisanang le ho lokolloa ha li-intermolecular crosslinking. Ka kakaretso index ea arylation ke 40-60%.
Mocheso o tlase oa mocheso oa carbonizationKa kakaretso ke 300-800 ℃, haholo-holo mocheso oa ho phatloha ha mocheso, haholo-holo o sebelisa mocheso o phahameng oa mocheso oa sebōpi sa motlakase, sethaleng se hlahisa khase e ngata ea ho tsoa le sekontiri,.
Litšobotsi: 'Mala oa fiber e entsoeng pele ho oxidized e tla ba lefifi, hangata e ntšo, empa e ntse e boloka morphology ea fiber, sebopeho sa ka hare se fetile tekanyo e itseng ea liphetoho tsa lik'hemik'hale, ho thehoa ha lihlopha tse ngata tse sebetsang tse nang le oksijene le sebopeho sa sefapano, ho rala motheo oa carbonization e latelang.
2. (Mocheso o phahameng) sethaleng sa carbonization, ke pele ho oxidation ea precursor sepakapakeng inert ka phahameng mocheso decomposition, ho tlosoa ha eona ho phaella ho carbon heteroatoms (tse kang oksijene, hydrogen, naetrojene, joalo-joalo), e le hore butle-butle carbonization, sebopeho sa carbon amorph kapa microcrystalline carbon sebopeho. Ts'ebetso ena ke mohato oa bohlokoa ho thehoeng ha skeleton ea carbon. Mocheso ka kakaretso o pakeng tsa 1000-1800 ℃, haholo-holo mocheso oa condensation, boholo ba li-heaters tsa graphite li sebelisetsoa ho futhumatsa.
Litšobotsi: Karolo e ka sehloohong ea thepa ea carbonized ke carbon, sebopeho ke boholo ba carbon amorphous kapa chaotic graphite structure, conductivity ea eona ea motlakase, thepa ea mochine ha e bapisoa le sehlahisoa sa pele ho oxidation se na le keketseho e kholo.
3. Graphitizationke phekolo e eketsehileng ea mocheso oa lihlahisoa tsa carbonization ka mocheso o phahameng ho khothalletsa sebopeho sa carbon ea amorphous kapa microcrystalline carbon ho ea ka mokhoa o hlophisehileng oa kristale ea graphite. Ka ketso ea mocheso o phahameng, liathomo tsa k'habone li hlophisoa bocha hore li thehe sebopeho sa lera la hexagonal se nang le maemo a holimo, ka hona ho ntlafatsa haholo matla a motlakase le a mocheso le matla a mochini oa thepa.
Litšobotsi: Sehlahisoa sa graphitized se na le sebopeho sa graphite se phahameng haholo, se fanang ka motlakase o motle haholo oa motlakase le mocheso, hammoho le matla a khethehileng a phahameng le modulus e khethehileng. Ka mohlala, high-moduluslikhoele tsa carbonli fumanoa ka tekanyo e phahameng ea graphitization.
Mehato e ikhethileng le litlhoko tsa lisebelisoa bakeng sa pre-oxidation, carbonization le graphitization:
Pre-oxidation: e etsoa moeeng ka mocheso o laoloang oa 200-300 ° C. Ho hlokahala hore ho sebelisoe tsitsipano ho fokotsa ho fokotseha ha fiber.
Carbonization: e etsoa sebakeng se se nang moea se nang le keketseho ea butle-butle ea mocheso ho 1000-2000 ° C.
Graphitization: e etsoa ka mocheso o phahameng haholo (2000-3000 ° C), hangata sebakeng se se nang letho kapa sebakeng se se nang moea.